Polyethylene Material
Basell
|
|
Basell Raw Material
Hostalen CRP 100 black
Polyethylene, High Density
Product Description
Hostalen CRP 100 black is a high density polyethylene (HDPE), black coloured similar RAL 9004 with high melt viscosity for extrusion, injection and compression molding. The product is classified as PE 100 and provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength. 
It is not intended for medical and pharmaceutical applications.
Product Characteristics:
|
Status
|
Commercial: Active
|
|
Test Method used
|
ISO
|
|
Availability
|
Europe, Asia-Pacific
|
|
Processing Method
|
Extrusion Pipe Sheet and Semi Finished Products
|
|
Typical Customer Applications
|
Gas Pipe, Industrial, Soil & Waste Pipe, Drinking Water Pipe
|
|
Typical Properties
|
Method
|
Value
|
Unit
|
|
Physical
|
|
Density
|
ISO 1183
|
0.959
|
g/cm³
|
|
Melt flow rate (MFR)
|
ISO 1133
|
|
|
|
(190°C/21.6kg)
|
|
6.4
|
g/10 min
|
|
(190°C/5.0kg)
|
|
0.23
|
g/10 min
|
|
Staudinger index Jg
|
ISO 1628
|
380
|
ml/g
|
|
Mechanical
|
|
Tensile Modulus (23 °C, v = 1 mm/min, Secant)
|
ISO 527-1, -2
|
900
|
MPa
|
|
Tensile Stress at Yield (23 °C, v = 50 mm/min)
|
ISO 527-1, -2
|
23
|
MPa
|
|
Tensile Strain at Yield (23 °C, v = 50 mm/min)
|
ISO 527-1, -2
|
9
|
%
|
|
Tensile Creep Modulus 1h
|
ISO 899-1
|
850 [2.0]
|
MPa
|
|
Note: [Test stress in MPa]
|
|
Tensile Creep Modulus 1000h
|
ISO 899-1
|
360 [2.0]
|
MPa
|
|
Note: [Test stress in MPa]
|
|
Maximum elongation TD
|
EN 638
|
>350
|
%
|
|
MRS classification
|
ISO/TR 9080
|
10
|
MPa
|
|
Flexural stress at 3,5% deflection
|
ISO 178
|
21
|
MPa
|
|
FNCT (4.0 MPa, 2% Arkopal N 100, 80°C)
|
ISO 16770
|
>1000
|
h
|
|
Flexural creep modulus
|
DIN 19537-2
|
|
|
|
(4 point loading method, 1 min-value)
|
|
1100
|
MPa
|
|
(4 point loading method, 24 h-value)
|
|
560
|
MPa
|
|
(4 point loading method, 2000 h-value)
|
|
330
|
MPa
|
|
Impact
|
|
Charpy notched impact strength
|
ISO 179
|
|
|
|
(23 °C)
|
|
26
|
kJ/m²
|
|
(-30 °C)
|
|
13
|
kJ/m²
|
|
Hardness
|
|
Shore hardness (Shore D (3 sec))
|
ISO 868
|
63
|
|
|
Thermal
|
|
Vicat softening temperature (VST/B/50 K/h (50 N))
|
ISO 306
|
74
|
°C
|
|
Oxidation induction time (OIT) (210°C)
|
EN 728
|
30
|
min
|
|
Additional Information
|
|
Carbon black content
|
ISO 6964
|
2.25
|
%
|
|
Odor treshold
|
EN 1622/EN 1240
|
< 2
|
|
|
|
|
Notes
|
|
Typical properties; not to be construed as specifications
|